ASTM B86-13

Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings

ASTM International , 02/01/2013

Publisher: ASTM

File Format: PDF

$30.00$60.00

Description

Standard By:ASTM International , 02/01/2013

Published:02/01/2013

Pages:7

File Size:1 file , 100 KB

Language:English

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1This specification covers commercial zinc, zinc-aluminum castings and continuous cast bar stock, as designated and specified in Table 1. Seven alloy compositions are specified and designated as follows:

Common	Traditional	ASTM ^A	UNS

Alloy 3	Zamak 3	AG 40A ^B	Z33525
Alloy 7	Zamak 7	AG 40B	Z33527
Alloy 5	Zamak 5	AC 41A ^B	Z35533
Alloy 2	Zamak 2	AC 43A	Z35545
ZA-8	ZA-8	...	Z35638
ZA-12	ZA-12	...	Z35633
ZA-27	ZA-27	...	Z35841

^A See Table 1, Footnote C.

^B SAE Specification, Nos. 903 and 925 conform to the requirements for alloys AG40A and AC41A, respectively.

TABLE 1 Chemical Requirements

Element	Alloy 3^A^,^B^,^C^,^D Zamak 3 (AG40A)	Alloy 7^A^,^B^,^C^,^D^,^E Zamak 7 (AG40B)	Alloy 5^A^,^B^,^C^,^D Zamak 5 (AC41A)	Alloy 2^A^,^C^,^,^D Zamak 2 (AC43A)	ZA-8^A^,^C^,^F ZA-8	ZA-12^A^,^C^,^F ZA-12	ZA-27^A^,^C^,^F ZA-27
	(Z33525)	(Z33527)	(Z35533)	(Z35545)	(Z35638)	(Z35633)	(Z35841)
Aluminum	3.7-4.3	3.7-4.3	3.7-4.3	3.7-4.3	8.0-8.8	10.5-11.5	25.0-28.0
Magnesium	0.02-0.06^G	0.005-0.020	0.02-0.06^G	0.02-0.06	0.01-0.03	0.01-0.03	0.01-0.02
Copper	0.1 max^H	0.1 max^E	0.7-1.2	2.6-3.3	0.8-1.3	0.5-1.2	2.0-2.5
Iron, max	0.05	0.05	0.05	0.05	0.075	0.075	0.075
Lead, max	0.005	0.003	0.005	0.005	0.006	0.006	0.006
Cadmium, max	0.004	0.002	0.004	0.004	0.006	0.006	0.006
Tin, max	0.002	0.001	0.002	0.002	0.003	0.003	0.003
Nickel	. . .	0.005-0.020	. . .	. . .	. . .	. . .	. . .
Zinc^I	remainder	remainder	remainder	remainder	remainder	remainder	remainder

^A For purposes of acceptance and rejection, the observed value or calculated value obtained from analysis should be rounded to the nearest unit in the last right-hand place of figures, used in expressing the specified limit, in accordance with the rounding procedure prescribed in Practice E29.

^B Zinc alloy castings may contain nickel, chromium, silicon, and manganese in amounts of 0.02, 0.02, 0.035, and 0.06 %, respectively. No harmful effects have ever been noted due to the presence of these elements in these concentrations and, therefore, analyses are not required for these elements, with the exception of nickel analysis for Z33527.

^C ASTM alloy designations were established in accordance with Practice B275. The UNS designations were established in accordance with Practice E527. The last digit of a UNS number differentiates between alloys of similar composition. The UNS designations for ingot and casting versions of an alloy were not assigned in the same sequence for all alloys.

^D When this material is required to conform to ISO 301, the chemical limits for thallium and indium each shall not exceed 0.001 %.

^E For the majority of commercial applications, a copper content up to 0.25 % will not adversely affect the serviceability of these die castings and should not serve as a basis for rejection, unless otherwise specified in the contract or purchase order between the producer and user.

^F Zinc-aluminum ingot for foundry and pressure die casting may contain chrome, manganese, or nickel in amounts of up to 0.01 % each or 0.03 % total. No harmful effects have ever been noted due to the presence of these elements in up to these concentrations and, therefore, analyses are not required for these elements.

^G Magnesium may be as low as 0.015 % provided that the lead, cadmium, and tin do not exceed 0.003, 0.003, and 0.001 %, respectively.

^H For the majority of commercial applications, a copper content of up to 0.7 % will not adversely affect the serviceability of die castings and should not serve as a basis for rejection, unless otherwise specified in the contract or purchase order between the producer and user, such as to meet the requirements of ISO 15201.

^I Determined arithmetically by difference.

1.2Zinc Alloys Z33525, Z33527, Z35533, and Z35545 are used primarily in the manufacture of pressure die castings. Zinc-Aluminum Alloys Z35638, Z35633, and Z35841 are used in the manufacture of both foundry and pressure die castings. These alloys are also fabricated into continuous cast bar stock used for prototyping and screw machine stock.

1.3The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4Systems of nomenclature used to designate zinc and zinc-aluminum (ZA) alloys used for casting are described in Appendix X1.

1.5This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

ASTM B86-13

Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings

ASTM B86-13 History

ASTM B86-23

ASTM B86-18

ASTM B86-18e1

ASTM B86-13

ASTM B86-11

ASTM B86-10e1

ASTM B86-10

ASTM B86-10a

ASTM B86-09

ASTM B86-09a

More ASTM Standards PDF

ASTM D2715-92(2012)

ASTM E161-12

ASTM D2737-12e1

ASTM B708-12